Heat stabilized sub-stoichiometric dielectrics

ABSTRACT

A sub-stoichiometric oxide, nitride or oxynitride layer in an optical stack, alone or in direct contact with one or two stabilizing layers, stabilizes the optical properties of the stack. The stabilizing layer(s) can stabilize the chemistry and optical properties of the sub-stoichiometric layer during heating. The change in optical characteristics of the sub-stoichiometric layer upon heating can counter the change in optical characteristics of the rest of the optical stack.

BACKGROUND OF THE INVENTION

1. Field of the Invention

The present invention relates to sub-stoichiometric dielectric materials. In particular, the present invention relates to sub-stoichiometric dielectric material layers used in optical stacks formed on transparent substrates.

2. Discussion of the Background

Sub-stoichiometric dielectrics are well known in the field of thin films and optical coatings. These sub-stoichiometric materials are typically substances, based on metals, silicon or germanium, that are less than fully reacted with oxygen or nitrogen. Frequently, these materials are optically absorbing in the visible wavelengths while the fully reacted corresponding compounds are often optically non-absorbing in the visible wavelengths.

Sub-stoichiometric materials in thin film form are often included into optical stacks. Compared to stoichiometric dielectric compounds, sub-stoichiometric dielectric materials have a number of desirable properties.

For example, a sub-stoichiometric dielectric generally has a higher index of refraction (“n”) than the corresponding stoichiometric dielectric, and may provide an optical stack with optical properties that are more difficult to reach with all lower index stoichiometric layers. The higher index of the sub-stoichiometric dielectric often allows the sub-stoichiometric layer to be thinner than the corresponding stoichiometric dielectric.

A sub-stoichiometric layer also generally has a higher extinction coefficient (“k”) than the corresponding stoichiometric dielectric. As a result, sub-stoichiometric dielectric materials allow optical stacks to achieve optical properties that cannot be reached with non-absorbing stoichiometric dielectric compounds only.

Thin films of metal sub-oxides and sub-nitrides generally have better properties as chemical barriers than the corresponding stoichiometric metal oxides and nitrides. Barrier layers of metal sub-oxides and sub-nitrides are useful in optical stacks to protect vulnerable metal layers from corrosion. The barrier layers reduce diffusion into the stack of reactive materials such as water or oxygen.

Deposition rates are usually higher for sub-stoichiometric oxide and nitride materials than for stoichiometric materials, As a result, the use of sub-stoichiometric layers typically decreases production costs for manufacturing thin film coatings. This is true for most sputtering and evaporation processes.

For some optical designs, it is desirable to block transmission of UV light. Most sub-stoichiometric materials tend to be more absorbing in the UV wavelengths than corresponding stoichiometric compounds.

An undesirable property of sub-stoichiometric thin film materials is that they tend to be more chemically reactive than fully oxidized or fully nitrided compounds. Often, a sub-stoichiometric layer in an optical stack will oxidize, particularly if the stack is heated or subjected to water or corrosive chemicals. Oxidation can result in a change in the layer's n and k values, which will change the spectral characteristics of an optical stack.

There is a need to stabilize the properties of optical stacks, particularly optical stacks containing sub-stoichiometric layers. This is particularly true when the stack is heated in an annealing or substrate tempering process.

SUMMARY OF THE INVENTION

The present invention provides an optical stack containing a sub-stoichiometric dielectric layer whose characteristics are controlled to stabilize the optical properties (e.g., transmission and reflection) of the stack.

In embodiments, the sub-stoichiometric layer can be directly contacted on one or both sides by a stabilizing or cladding layer that functions to stabilize the chemistry of the sub-stoichiometric layer. The stabilization function occurs, e.g., when the optical stack is exposed to elevated temperatures that would normally cause the sub-stoichiometric dielectric layer to react in air or another atmosphere. By hindering reaction of the sub-stoichiometric layer and stabilizing the chemistry of the optical stack, the stabilizing layer(s) can stabilize the optical properties of the stack, particularly when the sub-stoichiometric layer serves a primarily optical interference function in the stack.

In other embodiments, the composition and thickness of a sub-stoichiometric layer can be chosen so that reaction of the sub-stoichiometric layer with air or another atmosphere upon heating brings about a change in an optical property (e.g., optical absorption) that exactly balances the change in that property by the rest of the optical stack, so that the stack exhibits zero net change in the optical property.

BRIEF DESCRIPTION OF THE DRAWINGS

The preferred embodiments of this invention will be described in detail with reference to the following figures.

FIG. 1 shows index of refraction (“n”) and extinction coefficient (“k”) values for silicon aluminum nitride sputtered from a target of silicon containing 10 weight% aluminum in nitrogen sputtering gas.

FIG. 2 shows an optical stack including a sub-stoichiometric dielectric layer in direct contact with a stoichiometric dielectric stabilizing layer.

FIG. 3 shows an optical stack including a sub-stoichiometric dielectric layer sandwiched between and in direct contact with two stoichiometric dielectric stabilizing layers.

FIG. 4 shows index of refraction, n, and extinction coefficient, k, for a 39 nm thick NiCrOx sample before and after heating at 730° C. for four minutes in air.

FIG. 5 shows the change in transmission (Delta % TY) upon tempering of a single silver, low-emissivity optical stack containing a NiCrOx layer as a function of the NiCrOx layer thickness.

DETAILED DESCRIPTION OF PREFERRED EMBODIMENTS

The present invention provides sub-stoichiometric layers, alone or in combination with one or more stabilizing layers, that can stabilize the optical properties of an optical stack, particularly during heating and tempering.

Due to process limitations, multi-element compounds are rarely deposited in thin film layers with the exact ratio of elements dictated by stoichiometry.

In light of this, the term “stoichiometric” as used herein refers to an oxide, nitride or oxynitride, of one or more elements, in which the atomic ratio of oxygen and/or nitrogen relative to the other elements is within ±5% of the atomic ratio of oxygen and/or nitrogen in an oxide, nitride or oxynitride compound of the one or more elements. For example, “stoichiometric” tin oxide refers herein to SnO_(x), where 1.9≦x≦2.1. “Stoichiometric” silicon nitride refers herein to Si₃N_(y), where 3.8≦y≦4.2. A “stoichiometric” oxynitride of Si-10 wt % Al refers herein to (Si_(0.9)Al_(0.1))₃(O_(x)N_(y))_(w), where x+y=1; as x approaches 1, w approaches 6; and as y approaches 1, w approaches 4.

The term “sub-stoichiometric” as used herein refers to an oxide, nitride or oxynitride, of one or more elements, in which the atomic ratio of oxygen and/or nitrogen relative to the other elements is less than 95% and at least 30% of the atomic ratio of oxygen and/or nitrogen in the oxide, nitride or oxynitride compound of the one or more elements. For example, a “sub-stoichiometric” tin oxide refers herein to SnO_(x), where 0.6≦x<1.9. “Sub-stoichiometric” silicon nitride refers herein to Si₃N_(y), where 1.2≦y<3.8.

The atomic ratio of oxygen and/or nitrogen in a stoichiometric or sub-stoichiometric layer can be determined using various techniques well known in the art For example, measurements of n and k can be used to make an estimation of stoichiometry. Values of n and k for many stoichiometric oxides and nitrides are well documented in the literature and easily verified. n and k values for some standard samples of specific sub-stoichiometric materials can also be easily obtained. Comparison of these values with those of a particular stoichiometric or sub-stoichiometric layer can indicate the atomic ratio of oxygen and/or nitrogen in the particular layer. Surface analysis techniques such as x-ray photoelectron spectroscopy (XPS) and Rutherford backscattering (RBS) can also be used to determine stoichiometry.

The term “dielectric” as used herein refers to an oxide, nitride or oxynitride material, which can be “stoichiometric” or “sub-stoichiometric”, that is at least partially transparent to visible light and creates interference effects in thin films.

The term “homogeneous” as used herein describes a layer that does not have a gradient in chemical composition extending from one surface of the layer to the other surface of the layer. Thus, the term “homogeneous” describes a layer consisting of a single compound. The term “homogeneous” also describes a layer consisting of a uniform mixture of two or more different compounds.

In embodiments, the present invention provides an optical stack having a sub-stoichiometric dielectric layer in contact with one or two stabilizing layers. Preferably the stabilizing layers are in direct contact with the sub-stoichiometric layer.

The sub-stoichiometric layer is a sub-stoichiometric dielectric composition that can result from the reaction of oxygen and/or nitrogen with at least one metal element or semiconductor element. Suitable metal elements include transition metals, Mg, Zn, Al, In, Sn, Sb and Bi. Preferably, the metal elements include Mg, Y, Ti, Zr, Nb, Ta, W, Zn, Al, In, Sn, Sb and Bi. Suitable semiconductor elements include Si and Ge. The sub-stoichiometric layer can be doped with oxides, nitrides and oxynitrides of elements such as Ti, Fe and Cu that raise the n and k of the layer. Co-sputtering the dopants and the host material may produce a layer having a non-homogeneous composition, e.g, a layer in which the dopant concentration varies from top to bottom. Preferably, the sub-stoichiometric layer has a homogeneous composition.

The sub-stoichiometric layer preferably functions in an optical stack primarily as an optical interference layer. The sub-stoichiometric layer can have a thickness in a range of from 10 to 100 n, preferably from 15 to 80 nm, more preferably from 25 to 70 nm. If the sub-stoichiometric layer is less than 10 nm thick, then it may not sufficiently influence the optical interference. If the sub-stoichiometric layer is more than 100 nm thick, then it may absorb too much visible light and darken the optical stack.

As discussed above, the sub-stoichiometric dielectric layer can be in direct contact with one or two stabilizing layers. Materials that can be used in the stabilizing layer are those that reduce chemical and optical changes in the adjacent sub-stoichiometric layer upon exposure to heat. Preferably each stabilizing layer has a homogenous composition.

A stabilizing layer can be a metallic material that would tend to oxidize to a substantially transparent compound during a heating process in an oxygen-containing atmosphere. A metal stabilizing layer can comprise, e.g., Ti, Zr, Hf, Nb, Ta, Mo, W, Al, or Mg, and alloys, aluminides and silicides of these elements.

A stabilizing layer can also be a sub-stoichiometric dielectric. When the stabilizing layer is a sub-stoichiometric dielectric, the stabilizing layer has a different composition than that of the sub-stoichiometric layer contacted by the stabilizing layer. The sub-stoichiometric stabilizing layer upon heating may retain its sub-stoichiometric state or may oxidize to a more stoichiometric state.

Preferably, the stabilizing layer is a stoichiometric dielectric. A stoichiometric stabilizing layer can be a fully reacted version of the sub-stoichiometric layer contacted by the stabilizing layer, with the metal and/or semiconductor elements in the oxides, nitrides or oxynitrides of the stoichiometric layer being in their highest oxidation state (e.g., Nb₂O₅, with Nb⁵⁺). Alternatively, the stabilizing layer can be a stoichiometric version of the oxides, nitrides or oxynitrides of the sub-stoichiometric layer in which the elements are not in their highest oxidation state (e.g., NbO₂, with Nb⁴⁺). The stabilizing layer can also be a stoichiometric, partially or fully reacted, oxide, nitride or oxynitride of different elements than those present in the sub-stoichiometric layer.

The stoichiometric stabilizing layer(s) can be more or less absorbing to visible light than the sub-stoichiometric layer. Many elements, such as Mg, Y, Ti, Zr, Nb, Ta, W, Zn, Al, In, Sn, Sb, Bi and Ge, form sub-stoichiometric oxides, nitrides and oxynitrides that are more optically absorbing to visible light than is the most fully reacted stoichiometric oxide, nitride or oxynitride of the element. In contrast, some metals, such as Cr, Fe, Ni and Cu, have more than one stoichiometric oxidation state, and in some cases the most oxidized state is not the least absorbing to visible light. Heating a thin film of these oxides, and subsequently causing further oxidation, can result in a more optically absorbing layer. For example, Cu₂O and CuO are the two stoichiometric oxides of copper, and Cu₂O is the least absorbing in the visible wavelengths.

Oxides of Mg, Y, Ti, Zr, Nb, Ta, W, Zn, Al, In, Sn, Sb, Bi and Ge tend to have an extinction coefficient k of close to zero (essentially non-absorbing) throughout the visible wavelengths in the fully oxidized state. Nitrides of Al and Si follow the same trend. This non-absorbing characteristic makes stabilizing layers of these materials very useful in optical stacks. For many optical designs, absorption is highly undesirable. However, there are some optical designs where absorption is acceptable or desirable.

FIG. 1 compares index of refraction and extinction coefficient values for sub-stoichiometric and stoichiometric SiAlO_(x)N_(y) sputtered films. FIG. 1 shows that sub-stoichiometric SiAlO_(x)N_(y) has a higher index of refraction and higher extinction coefficient than stoichiometric SiAlO_(x)N_(y).

The stabilizing layer functions primarily to chemically stabilize the sub-stoichiometric layer. Preferably, the stabilizing layer(s) in contact with the sub-stoichiometric layer allow the sub-stoichiometric layer to be heated to a temperature of 600° C., more preferably 700° C., even more preferably 800° C., for 4 to 5 minutes with little or no change in optical properties.

A stabilizing, or cladding, layer can have a thickness in a range of from 1 to 10 nm, preferably 2 to 8 nm, more preferably from 2 to 5 nm.

In embodiments, the index of refraction of the sub-stoichiometric layer can be at least 1.8 (i.e., n≧1.8), preferably at least 2.3 (i.e., n≧2.3). The extinction coefficient of the sub-stoichiometric layer, k, can be in a range of 0.03≦k≦0.15.

The oxide, nitride or oxynitride of the sub-stoichiometric layer dielectric can have a higher index of refraction than the stabilizing layer(s) and can be thicker than the one or more stabilizing layers. This can result in a combination of sub-stoichiometric and stoichiometric layers with a higher index of refraction than a stoichiometric layer of the same thickness as the combination.

Alternatively, the oxide, nitride or oxynitride of the sub-stoichiometric layer dielectric can have a lower index of refraction than the stabilizing layer(s). The combination with one or more stabilizing layers with such a low index sub-stoichiometric layer can create the equivalent of a layer having a much higher index of refraction than the sub-stoichiometric layer.

When the sub-stoichiometric layer is sandwiched between two stabilizing layers, the two stabilizing layers can have the same or different compositions, and the same or different thicknesses.

The optical stack of the present invention can be made by conventional thin film deposition techniques, such as sputtering, in which laminates of various layers are formed by vapor depositing the layers sequentially.

Optical stacks of various metal and dielectric layers can reduce the emissivity of transparent substrates, such as glass. FIG. 2 illustrates a low-emissivity (“low-e”) optical stack 20 deposited on a glass substrate 21. The optical stack 20 includes metal layers 24 and 27, which can comprise an infrared radiation reflecting metal such as Ag, Cu or Au. Between glass substrate 21 and metal layer 24 is sub-stoichiometric dielectric layer 22 in direct contact with stoichiometric dielectric layer 23. Between metal layers 24 and 27 is sub-stoichiometric dielectric layer 25 in direct contact with stoichiometric dielectric layer 26.

FIG. 3 illustrates a low-e optical stack 30 deposited on a glass substrate 31. The optical stack 30 includes metal layers 35 and 39, which can comprise an infrared radiation reflecting metal such as Ag, Cu or Au. Between glass substrate 31 and metal layer 35 is sub-stoichiometric dielectric layer 33 sandwiched between and in direct contact with stoichiometric dielectric layers 32 and 34. Between metal layers 35 and 39 is sub-stoichiometric dielectric layer 37 sandwiched between and in direct contact with stoichiometric dielectric layers 36 and 38.

In FIGS. 2 and 3, the designation “. . . ” indicates the presence of one or more unspecified layers.

In other embodiments of the present invention, an optical stack is provided in which the composition and thickness of the sub-stoichiometric layer is chosen so that the change in optical properties of the sub-stoichiochiometric layer upon heating offsets the change in optical properties of the remainder of the stack. Upon heating during tempering, some sub-stoichiometric materials, such as sputtered sub-stoichiometric NiCrO_(x), become more absorbing to visible light and exhibit an increase in index of refraction. In contrast, most low-e optical stacks become more transparent and lighten during tempering. Selection, by techniques well known in the art, of a suitable thickness of a suitable sub-stoichiometric material that becomes more absorbing to visible light upon heating will allow optical stacks to be designed that when heated during tempering undergo an absolute change in transmission (change in % TY) of 1.00% or less, preferably 0.50% or less, more preferably 0.25% or less (i.e., a change in transmission of ±1.00% or less, ±0.50% or less, or ±0.25% or less, respectively). Sub-stoichiometric NiCrO_(x) having a thickness of from 2 to 20 nm preferably 3 to 12 nm, can be used to counter the increase in transmission on heating. If the NiCrO_(x) layer is too thin, then it will be unable to counter the transmission changes in the other stack layers. If NiCrO_(x) is too thick, it will overcome the transmission increase of the other stack layers and the optical stack will overall become less transparent and darken upon tempering. The thickness of the NiCrO_(x) can be designed to exactly balance the tendency of the other layers to lighten and create a zero tempering transmission change. Preferably the sub-stoichiometric NiCrO_(x) layer is homogeneous.

EXAMPLES

Examples of low-e coatings on glass utilizing the present invention are shown in the examples below. Dielectric coatings were formed by midfrequency (˜30 kHz), dual magnetron sputtering onto room temperature substrates. SiAlO_(x)N_(y) was sputtered from a SiAl target in an Ar/O₂/N₂ atmosphere. ZnO was sputtered from a Zn target in an Ar/O₂ atmosphere. (Si_(0.9)Al_(0.1))O_(x)N_(y) was sputtered from a target containing Si and 10 wt % Al. Ag was DC sputtered from an Ag target in an Ar atmosphere. NiCrO_(x) was DC sputtered from a NiCr target in an Ar/O₂ atmosphere.

The stoichiometry of oxides, nitrides and oxynitrides was controlled by controlling the compositions of the sputtering target and the sputtering atmosphere. Optical transparency was used to confirm the stoichiometry of stoichiometric nitrides containing silicon and stoichiometric oxynitrides containing silicon.

Example 1

A comparison was made of the change in optical properties upon tempering of a sub-stoichiometric SiAlO N, layer not in contact with a stabilizing stoichiometric SiAlO_(x)N_(y) layer relative to the same sub-stoichiometric SiAlO_(x)N_(y) layer when in direct contact with a stabilizing stoichiometric SiAlO_(x)N_(y) layer.

In this comparison, low-e optical stacks containing a single Ag layer were deposited on soda-lime glass substrates (5 cm×5 cm×0.3 cm). Tables 1 and 2 show the numerical order in which various layers were deposited. Table 1 shows the deposition conditions used to form an optical stack in which the sub-stoichiometric SiAlO_(x)N_(y) layer was not in contact with a stabilizing stoichiometric SiAlO_(x)N_(y) layer. Table 2 shows the deposition conditions used to form another optical stack in which the sub-stoichiometric SiAlO_(x)N_(y) layer was in direct contact with a stabilizing stoichiometric SiAlO_(x)N_(y) layer.

The size of each of the two sputtering targets used to deposit SiAlO_(x)N_(y) by dual magnetron sputtering was 1 m×110 mm, for an effective target surface area of 0.11 m². The SiAlO_(x)N_(y) was sputtered at a power of 17.8-18.0 kW, for a power density of about 16.3 W/cm². Sub-stoichiometric SiAlO_(x)N_(y) was obtained by sputtering with a N₂ gas flow of 83 sccm. Stoichiometric SiAlO_(x)N_(y) was obtained by sputtering with a N₂ gas flow of 98 sccm. TABLE 1 Gas Flow Ar O₂ N₂ AC Power No. Layer (sccm) (sccm) (sccm) (kW) 1 SiAlO_(x)N_(y)(*) 100 10 83 17.8 2 ZnO 50 165 0 14.4 3 Ag 33 3 — — 4 NiCrO_(x) 50 37 — — 5 SiAlO_(x)N_(y) 100 10 98 17.9 (*)Sub-stoichiometric SiAlO_(x)N_(y)

TABLE 2 Gas Flow Ar O₂ N₂ AC Power No. Layer (sccm) (sccm) (sccm) (kW) 1 SiAlO_(x)N_(y)(**) 100 10 98 17.9 2 SiAlO_(x)N_(y)(*) 100 10 83 18 3 ZnO 50 165 0 14.4 4 Ag 33 3 — — 5 NiCrO_(x) 50 37 — — 6 SiAlO_(x)N_(y) 100 10 98 17.9 (*)Sub-stoichiometric SiAlO_(x)N_(y) (**)Stabilizing stoichiometric SiAlO_(x)N_(y)

The coated substrates were tempered in a muffle furnace at 730° C. for 4 minutes.

Table 3 shows the color change (ΔE) that resulted from the tempering. ΔE(Lab) is the color change including L, a* and b* values. ΔE(ab) is the color including color only (a* and b*) but not intensity (L). TABLE 3 Table 1 stack Table 2 stack (no stabilizing layer) (with stabilizing layer) ΔE(Lab) ΔE(ab) ΔE(Lab) ΔE(ab) T 2.0 1.5 2.3 1.5 Rg 3.6 3.6 3.1 3.0 Rf 4.4 4.4 3.7 3.7 T = transmission Rg = glass (uncoated) side reflected color Rf = thin film coated side reflected color

Table 3 shows that the transmission color change was not decreased by the stabilizing stoichiometric SiAlO_(x)N_(y) layer. In contrast, Table 3 shows that the reflected color change was decreased by the addition of the stabilizing stoichiometric SiAlO_(x)N_(y) layer in direct contact with the sub-stoichiometric SiAlO_(x)N_(y) layer. In particular, the decrease in glass side reflected color change (i.e., Rg ΔE) was 0.5 to 0.6 color units. Table 3 shows that the properties of an optical stack including a sub-stoichiometric SiAlO_(x)N_(y) layer can be stabilized by directly cladding the sub-stoichiometric SiAlO_(x)N_(y) layer with a stabilizing stoichiometric SiAlO_(x)N_(y) layer.

Example 2

Two single silver low-emissivity optical stacks were made. The first stack had a single sub-stoichiometric (Si_(0.9)Al_(0.1))O_(x)N_(y) bottom dielectric. The second stack had a thermally stabilizing stoichiometric (Si_(0.9)Al_(0.1))O_(x)N_(y) layer between the sub-stoichiometric (Si_(0.9)Al_(0.1))O_(x)N_(y) and the glass substrate. On top of each stack were identical (Si_(0.9)Al_(0.1))O_(x)N_(y) layers. The complete stack designs are shown below:

First Stack:

Glass/sub-stoichiometric (Si_(0.9)A_(0.1))O_(x)N_(y)/ZnO/Ag/NiCrO_(x)/(Si_(0.9)Al_(0.1))O_(x)N_(y)

Second Stack:

Glass/stoichiometric (Si_(0.9)Al_(0.1))O_(x)N_(y)/sub-stoichiometric (Si_(0.9)Al_(0.1))O_(x)N_(y)/ZnO/Ag/NiCrO_(x)/(Si_(0.9)Al_(0.1))O_(x)N_(y)

Both samples were tempered and checked for color change from tempering. The color change expressed as ΔE a* b* was calculated by the following equation: ΔE a*b*=(a* _(BB) −a* _(AB))²+(b* _(BB) −b* _(AB))²]^(0.5) where BB refers to color before tempering and AB refers to color after tempering.

The tempering color change for transmission (T ΔE a* b*), glass side reflection (Rg ΔE a* b*) and film (i.e., stack) side reflection (Rf ΔE a* b*) are shown in the following Table 4. TABLE 4 First stack: without Second stack: with stoichiometric stoichiometric (Si_(0.9)Al_(0.1))O_(x)N_(y) (Si_(0.9)Al_(0.1))O_(x)N_(y) stabilization layer stabilization layer T ΔE a* b* 1.5 1.5 Rg ΔE a* b* 3.6 3.0 Rf ΔE a* b* 4.4 3.7

Table 4 shows that the addition to the second stack of the protective stabilizing layer of stoichiometric (Si_(0.9)Al_(0.1))O_(x)N_(y) resulted in a reduction in tempering color shift for both glass side reflection and film (optical stack) side reflection.

In embodiments of the present invention, the stabilizing layer results in a tempering color shift for glass side reflection of 4.0 or less, preferably 3.5 or less, more preferably 3.0 or less, even more preferably 2.5 or less. In addition, the stabilizing layer results in a tempering color shift for film (optical stack) side reflection of 4.0 or less, preferably, 3.5 or less, more preferably 3.0 or less, even more preferably 2.5 or less.

Example 3

The following optical stack was prepared:

6 mm glass substrate/20 nm stoichiometric SiAlO_(x)N_(y)/8 nm ZnO/12 nm Ag/2 nm NiCrO_(x)/5 nm stoichiometric SiAlO_(x)N_(y)/55 nm sub-stoichiometric SiAlO_(x)N_(y)/5 nm stoichiometric SiAlO_(x)N_(y)/8 nm ZnO/15 nm Ag/2 nm NiCrO_(x)/36 nm stoichiometric SiAlO_(x)N_(y)

The SiAlO_(x)N_(y) was sputtered from a target containing Si and 10 wt % Al.

In this optical stack the middle dielectric (i.e. stoichiometric SiAlO_(x)N_(y)/sub-stoichiometric SiAlO_(x)N_(y)/stoichiometric SiAlO_(x)N_(y)) is primarily a higher index version of SiAlO_(x)N_(y). This allows a lower physical thickness for the layer and a higher sputtering rate in the deposition process.

The middle dielectric combination was deposited under the conditions shown in Table 5. TABLE 5 Gas Flow Ar O₂ N₂ AC Power (sccm) (sccm) (sccm) (kW) Stoichiometric 100 10 90 14.2 SiAlO_(x)N_(y) Sub-stoichiometric 100 10 83.5 14.2 SiAlO_(x)N_(y)

The color of the optical stack is very sensitive to the index and optical thickness of the middle layers. Normally, glass tempering at a temperature of 730° C. for 4 minutes would change the index and optical thickness. However, this change is reduced by the stabilizing stoichiometric layers clad on both sides of the sub-stoichiometric layer.

Example 4

Tin zinc oxide (SnZnO_(x)) is a common dielectric material used in temperable low-emissivity designs. For creating certain optical effects in thin film designs, SnZnO_(x) can be deposited in a sub-stoichiometric state.

An investigation was carried out to determine if optically absorbing, sub-stoichiometric SnZnO_(y)N_(x) could be thermally stabilized using stoichiometric SiAlO_(y)N_(x) layers. Thin film structures were formed on quartz substrates as illustrated in the following Table 6. TABLE 6 Layer 1 Layer 2 Layer 3, Sample 5 nm thick 25 nm thick 5 nm thick 1 SiAlO_(x)N_(y)** SnZnO_(x)N_(y)* SiAlO_(x)N_(y)** 2 SiAlO_(x)N_(y)** SnZnO_(x)N_(y)* 3 SnZnO_(x)N_(y)* SiAlO_(x)N_(y)** 4 SnZnO_(x)N_(y)* *Sub-stoichiometric **Stabilizing stoichiometric

The layers were sputtered from 1 meter long Twin-Mag targerts. Nitrogen was added to the sub-stoichiometric SnZnO_(x)N_(y) to stabilize the sputtering process and reduce arcing. Run conditions for the SiAlO_(x)N_(y) and the SnZnO_(x)N_(y) are shown in the following Table 7. TABLE 7 Ar O₂ N₂ Line AC flow flow flow speed Thick power I V Pressure Layer (sccm) (sccm) (sccm) (m/min) (nm) (kW) (amps) (volts) (mbar) SiAlO_(y)N_(x) 100 10 115 7.562 5 17.1 27.2 831 6.1E−3 SnZnO_(y)N_(x) 80 176 60 3.267 25 11.9 14.6 471 5.7E−3

After the four samples were deposited, percent optical absorption was measured in the visible wavelengths before and after baking. Baking was done at 670° C. for 5 minutes The change in percent optical absorption from the samples before bake to after bake at a wavelength of 400 nm is shown in Table 8 below. TABLE 8 Change in percent absorption Layer Structure at 400 nm wavelength SnZnO_(x)N_(y)* −5.4 SiAlO_(x)N_(y)**/SnZnO_(x)N_(y)* −2.01 SnZnO_(x)N_(y)*/SiAlO_(x)N_(y)** −4.18 SiAlO_(x)N_(y)**/SnZnO_(x)N_(y)*/SiAlO_(x)N_(y)** −2.84 *Sub-stoichiometric **Stabilizing stoichiometric

Table 8 shows that the absorption decrease due to heating was less for the samples with a stoichiometric SiAlO_(x)N_(y) layer.

A similar investigation was made to determine if stoichiometric SnZnO_(x) layers would stabilize optically absorbing, sub-stoichiometric SnZnO_(x)N_(y). In these stacks, the decrease in absorption with heating was the same with and without the SnZnO_(x) layers.

Example 5

Double silver low emissivity stacks with two NiCrO_(x) layers were made as shown below: Glass/SiAlO_(x)N_(y)/ZnO/Ag/NiCrO_(x)/SiAlO_(x)/Ny/ZnO/Ag/NiCrO_(x)/SiAlO_(x)N_(y)

In one version of the stack, the NiCrO_(x) layers were approximately 2 nm thick. In a second version of the stack, the NiCrO_(x) layers were approximately 4 nm thick. Optical transmission (TY) was measured before and after baking the stacks at 730° C. for four minutes. The results are shown in the following Table 9. TABLE 9 Estimated TY TY DC Ar O2 Transport NiCrO_(x) before after power flow flow speed thickness tempering tempering (kW) (sccm) (sccm) (m/min) (nm) (%) (%) ΔTY 3.67 50 37 8 2 75.13 80.50 5.37 3.67 50 37 4 4 75.25 77.27 2.02

Table 9 shows that the optical stack with the thicker NiCrO_(x) has a smaller transmission change (ΔTY) upon heating. The decrease in ΔTY with increase in NiCrO_(x) thickness indicates that NiCrO_(x) decreases in transmission and becomes more optically absorbing upon heating.

Example 6

The index of refraction, n, and extinction coefficient, k, of a 39 nm thick NiCrO_(x) film deposited on a quartz subtrate were measured as a function of wavelength using a Woollam M2000U Ellipsometer before baking. After baking at 730° C. for four minutes in air, the optical constants were measured again. As shown in FIG. 4, both n and k for the NiCrO_(x) were increased by the heating.

Example 7

Four single silver low-emissivity optical stacks were made in which only the thickness of the NiCrO_(x) barrier layer, deposited on the Ag layer, was varied. The optical stacks had the following general design:

Glass/3.5 nm stoichiometric SiAlO_(x)N_(y)/17 nm sub-stoichiometric SiAlO_(x)N_(y)/6 nm ZnO/13.4 nm Ag/NiCrO_(x)/38 nm stoichiometric SiAlO_(x)N_(y) The NiCrO_(x) was reactively DC sputtered from 1 meter long 80 wt % Ni-20 wt % Cr target. The SiAlO_(x)N_(y) was sputtered from a target containing Si and 10 wt % Al. The sputtering conditions are shown in the following Table 10. TABLE 10 NiCrO_(x) Sputtering Conditions Sputtering Ar flow O₂ flow DC power Current Target Pressure (sccm) (sccm) (kW) (amps) Voltage (mbar) 50 37 2.23 3.6 624 1.18E−3

In the standard or control stacks, the NiCrO_(x) layers were approximately 2 nm thick. The thickness of the NiCrO_(x) layer was increased in the other stacks.

The stacks were tempered by heating in air at 670° C. for 6 minutes, 20 seconds.

The transmission (% TY) was measured before and after hex ting. The results are shown in the following Table 11 and in FIG. 5. TABLE 11 NiCrOx Thickness Before Temper After Temper Delta TY (nm) % TY % TY (change in % TY) 2.2 82.1 85.6 3.5 2.2 82.3 85.6 3.4 4.3 81.8 83.1 1.3 8.7 79.7 80.1 0.5 17.4 73.5 71.8 −1.7

Table 11 and FIG. 5 show that the change in % TY upon tempering decreased with increasing NiCrO_(x) thickness and became negative above a NiCrO_(x) thickness of about 10.5 nm. These results predict that a NiCrO_(x) thickness of about 10.5 nm in the optical stack will result in an optical stack that exhibits zero transmission change upon tempering. These results also indicate that zero transmission change upon tempering can be achieved in optical stacks containing two or more silver layers by proper selection of NiCrO_(x).

Both before and after the tempering, the optical stacks were tested for wet brush durability using a standardized procedure involving brushing under water. The brushing damage on each sample was visually quantified using a standard scale. The results are show in Table 12 below, in which “% damage” refers to the surface area damaged by brushing. TABLE 12 % damage % damage NiCrOx thickness caused by wet brushing caused by wet brushing (nm) before tempering after tempering 2.2 0 40 2.2 0 40 4.3 0 10 8.7 0 2 17.4 0 0

Table 12 shows that before tempering the optical stacks were not damaged by the wet brushing. In contrast, after the tempering the stacks with the thinnest NiCrO_(x) layers exhibited the most surface damage, but the amount of wet brush damage decreased with increasing NiCrO_(x) thickness.

The disclosure herein of a range of values is a disclosure of every numerical value within that range. In addition, the disclosure herein of a genus is a disclosure of every species within the genus (e.g., the disclosure of the genus “transition metals” is a disclosure of every transition metal species, such as Nb, Ta, etc.).

While the present invention has been described with respect to specific embodiments, it is not confined to the specific details set forth, but includes various changes and modifications that may suggest themselves to those skilled in the art, all falling within the scope of the invention as defined by the following claims. 

1-16. (canceled) 17: A method of making an optical stack, the method comprising laminating a stabilizing layer and a sub-stoichiometric layer; and producing an optical stack comprising the sub-stoichiometric layer in direct contact with the stabilizing layer, wherein the sub-stoichiometric layer consists of a homogeneous sub-stoichiometric composition selected from the group consisting of oxides, nitrides and oxynitrides, where the sub-stoichiometric composition comprises at least one element selected from the group consisting of metal elements and semiconductor elements, and the sub-stoichiometric composition further comprises a sub-stoichiometric amount of at least one element selected from the group consisting of oxygen and nitrogen; the stabilizing layer comprises the at least one element selected from the group consisting of metal elements and semiconductor elements, and a stoichiometric amount of the at least one element selected from the group consisting of oxygen and nitrogen; and the sub-stoichiometric layer is from 10 to 100 nm thick and thicker than the stabilizing layer. 18-36. (canceled) 37: A method of making an optical stack, the method comprising laminating a first stabilizing layer, a sub-stoichiometric layer and a second stabilizing layer; and producing an optical stack comprising the sub-stoichiometric layer sandwiched between and in direct contact with the first stabilizing layer and the second stabilizing layer, wherein the sub-stoichiometric layer consists of a sub-stoichiometric composition selected from the group consisting of oxides, nitrides and oxynitrides, where the sub-stoichiometric composition comprises at least one element selected from the group consisting of metal elements and semiconductor elements, and the sub-stoichiometric composition further comprises a sub-stoichiometric amount of at least one element selected from the group consisting of oxygen and nitrogen; and the first stabilizing layer and the second stabilizing layer each comprises the at least one element selected from the group consisting of metal elements and semiconductor elements, and a stoichiometric amount of the at least one element selected from the group consisting of oxygen and nitrogen. 38-39. (canceled) 40: A method of making an optical stack, the method comprising tempering an optical stack comprising a homogeneous sub-stoichiometric layer of sub-stoichiometric NiCrO_(x), wherein the sub-stoichiometric layer is from 2 to 20 nm thick; and during the tempering the absolute change in transmission of the optical stack is 1.00% or less. 